Ahmadi S, Eftekhari yekta B, mirhabibi A. Synthesis and Photocatalytic Properties of Sol-Gel Derived B₂O₃-SiO₂-TiO₂ Glass-Ceramic Coatings. IJMSE 2025; 22 (3) :1-8
URL: http://ijmse.iust.ac.ir/article-1-3885-en.html
Abstract:   (2708 Views)
The crystallization behavior and photocatalytic properties of the sol-gel derived glass ceramic coatings in the TiO2-SiO2-B2O3 system were studied. the prepared sol was sprayed on a glazed ceramic wall. Following drying, the coated specimens were fired at 900°C for 1 h. The impact of boron oxide content in the composition was explored in terms of anatase stability and glass maturing temperature. The thermal and crystallization behaviors of the dried gels were studied by the STA, XRD, and FESEM. The photocatalytic property of the coated layer was examined using methylen blue degradation. Based on the results, the sample containing 15 wt% of boron oxide demonestrated about  30% dye removal efficiency, after only 60 min of UV-irradiation. Additionally, this particular sample exhibited the greatest magnitude of the anatase phase in comparison to the other samples.
 
Full-Text [PDF 792 kb]   (807 Downloads)    

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb